A335 P5/P9/P11 Seamless Carbon Alloy Boiler Steel Pipe

A335 P5/P9/P11 Seamless Carbon Alloy Boiler Steel Pipe

Get Latest Price

Payment Type:	L/C,T/T,D/P
Incoterm:	FOB,CFR,CIF,EXW
Transportation:	Ocean,Land,Express
Port:	Tianjin,Qingdao,Shanghai

Contact Now

Product Description

Product Attributes

Model No.: A335 P5/P9/P11

Standard: Bs, Gb, Astm, Jis, Din, Api

Material: A53-A369, 10#-45#, Cr-Mo Alloy, Crni Alloy, Mn-V Alloy

Section Shape: Round

Application: Fluid Pipe, Boiler Pipe, Structure Pipe

Production Process: Hot Rolled

Certification: Api, Ce

Special Tube: Api Pipe

Whether Alloy: Is Alloy

Tolerance: ±1%

Category: Seamless Steel Pipe

Processing Service: Cutting, Punching, Decoiling, Bending

Packaging & Delivery

Selling Units	:	Ton
Package Type	:	Standard marine packaging, or as required by the customer
Picture Example	:

Boiler Alloy Steel Pipe

ASTM A53 A106 Round Carbon Seamless Steel Pipe



Product Description

ASTM A335 Alloy Boiler Steel Pipe

Standard specification for seamless ferritic alloy-steel pipe for high-temperature service.

ASTM A335 Pipe (ASME S/A335, Chorme-Moly) is a seamless ferritic Alloy-Steel Pipe for high temperature service. Pipe ordered to this specification shall be suitable for bending, flanging (vanstoning), and similar forming operations, and for fusion welding. Sometimes referred to as “P Grade”, Chrome Moly Pipe is popular in P-Grades P5, P9, P11, P22, and P91. The most common use of grades P11, P22, and P91 is in the power industry and petro-chemical plants, Grades P5 and P9 are commonly used in refineries.

A335 is often called chrome moly pipe because of the chemical makeup of Molybdenum (Mo) and Chromium (Cr). Molybdenum increases the strength of steel as well as the elastic limit, resistance to wear, impact qualities, and hardenability. Moly increases the resistance to softening, restrains grain growth and makes chromium steel less susceptible to embrittlement. Moly is the most effective single additive that increases high temperature creep strength. It also enhances the corrosion resistance of steel, and inhibits pitting. Chromium (or chrome) is the essential constituent of stainless steel. Any steel with 12% or more Chrome is considered stainless. Chrome is virtually irreplaceable in resisting oxidation at elevated temperatures. Chrome raises the tensile, yield, and hardness at room temperatures. The composition chrome moly alloy steel pipe make it ideal for use in power plants, refineries, petro chemical plants, and oil field services where fluids and gases are transported at extremely high temperatures and pressures.

ASTM A335 P11

Stocks a full range of the following A335 pipe grades:

Standard Specification for Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes.

This specification covers seamless ferritic and austenitic steel boiler, superheater, and heat-exchanger tubes. Grades containing the letter H in their designation have requirements different from those of similar grades not containing the letter H. These different requirements provide higher creep-rupture strength than normally achievable in similar grades without these different requirements. The tubes shall be made by the seamless process and shall be either hot finished or cold finished, as specified. Grade TP347HFG shall be cold finished. Heat treatment shall be done separately and in addition to heating for hot forming. The ferritic alloy and ferritic stainless steels shall be reheated. On the other hand, austenitic stainless steel tubes shall be furnished in the heat-treated condition. Alternatively, immediately after hot forming, while the temperature of the tubes is not less than the minimum solution temperature, tubes may be individually quenched in water or rapidly cooled by other means. Tension test, hardness test, flattening test, and flaring test shall be done to each tube. Also, each tube shall be subjected to the nondestructive electric test or hydrostatic test.

Product Specification

Item	Cold rolled/Hot rolled alloy steel Seamless Pipe
Standard	ASTM A209M/ASME 209M, ASME SA210, ASTM A213/ASME SA213M ASTM A333M/ASME SA333/SA333M, ASTM A334M/ASME SA334/SA334M ASTM A335/ASME SA335, ASTM A519, ASTM A691 GB3087, GB6479-2000, GB9948-2006, GB5310-2013, GB5310-95, GB9948-88 DIN 17175, EN10216-2, JISG3467, JISG3458, JIS G3441, NF A49-213/215, BS3059, BS3604, BS3606
Materials	A209 T1/SA209 T1, A209 T1b/SA-209 T1b, A209 T1a/SA209 T1a. T2, T5, T9, T11, T12, T22, T23, T24, T91, T911, T92, T122. P1, P2, P5, P5b, P5c, P9, P11, P12, P21, P22, P23, P24, P91, P92. 4118, 4130, 4135, 4137, 4140. 20G, 25MnG, 15MoG, 15CrMoG, 20MoG, 12CrMoG, 12Cr2MoG, 12Cr1MoVG, 12Cr2MoWVTiB, 10Cr9Mo1VNb, 15CrMoG, 10CrMo910. ST35.8, ST45.8, 15Mo3, 13CrMo44, 10CrMo910, 14MoV63,12Cr1MoV. P195GH, P235GH, P265GH, 13CrMo4-5, 10CrMo9-10, 16Mo3, 10CrMo5-5, X10CrMoVNb9-1. GRADE 91, CM65, CM70, CM75, CMSH70, CMS75, CMSH80. GRADE 1/2 Cr, GRADE 1CR, GRADE 1 1/4 CR, 2 1/4 Cr, 3CR, 5CR, 9CR. STPA12, STPA20, STPA22, STPA23, STPA24, STPA25, STPA26. SCR420 TK,SCM415 TK, SCM418 TK, SCM420TK, SCM430TK, SCM435TK, SCM440TK. TU15D3, TU13CD4-04, TU10CD910, TUZ10CD505. S1-622-440, S2-622-440, S1-622-490, S2-622-490, S1-629-470, S2-629-470, S2-629-590. HFS625 CFS625, CFS625.
Description	Surface	black painted, PE coated, galvanized
	Length	5.8m, 6m, 11.8m, 12m, or as required
	Wall Thickness	1-120mm
	Outer Diameter	6-1200mm
Trade terms	Payment terms	T/T, L/C, D/P
	Price terms	FOB, CIF
Package	Standard export seaworthy package or as required.
Delivery time	Prompt delivery or as the order quantity.
Export to	Alloy steel pipe applies to petroleum,chemical industry, electric power, boiler, high temperature resistant, low temperature resistant,corrosion resistant Seamless Steel Pipe used.Alloy steel pipealso can made according to the customer.
Container size	20ft GP:5898mm(Length)x2352mm(Width)x2393mm(High) 24-26CBM 40ft GP:12032mm(Length)x2352mm(Width)x2393mm(High) 54CBM 40ft HC:12032mm(Length)x2352mm(Width)x2698mm(High) 68CBM
Contact	If you have any question,please feel free to contact me.

Chemical Composition(%) of ASTM A335 pipe

ASTM Specification pipe confirming to ASTM A335 shall have the following chemical properties. Tensile and Hardness Requirements The tensile properties of the ASTM A335 pipe shall conform to the requirements as prescribed. Pipe of Grades P91, P92, and P122 shall have a hardness not exceeding 250 HB/265 HV [25 HRC]. For pipe of Grades P91, P92, P122, and P911, Brinell, Vickers, or Rockwell hardness tests shall be made on a specimen from each lot (see Note 7). These pipe bear high resistance to rupture at high temperature and pressures. With hydrogen crack resistance and sulfide stress corrosion cracking chrome moly pipe are highly preferred over Carbon pipe.

Grade	C	Mn	P max	S max	Si	Cr	Mo	V	N	Others
P1	0.1-0.2	0.3-0.8	0.025	0.025	0.1-0.5	1.0-1.5	0.44-0.65	/	/	/
P2	0.1-0.2	0.3-0.61	0.025	0.025	0.1-0.3	0.5-0.81	0.44-0.65	/	/	/
P5	≤0.15	0.3-0.6	0.025	0.025	≤0.5	4.0-6.0	0.45-0.65	/	/	/
P5b	≤0.15	0.3-0.6	0.025	0.025	1.0-2.0	4.0-6.0	0.45-0.65	/	/	/
P5c	≤0.12	0.3-0.6	0.025	0.025	≤0.5	4.0-6.0	0.45-0.65	/	/	/
P9	≤0.15	0.3-0.6	0.025	0.025	0.25-1.0	8.0-10.0	0.9-1.1	/	/	/
P11	0.05-0.15	0.3-0.6	0.025	0.025	0.5-1.0	1.0-1.5	0.44-0.65	/	/	/
P12	0.05-0.15	0.3-0.61	0.025	0.025	≤0.5	0.8-1.25	0.44-0.65	/	/	/
P15	0.05-0.15	0.3-0.6	0.025	0.025	1.15-1.65	/	0.44-0.65	/	/	/
P21	0.05-0.15	0.3-0.6	0.025	0.025	≤0.5	2.65-3.35	0.8-1.06	/	/	/
P22	0.05-0.15	0.3-0.6	0.025	0.025	≤0.5	1.9-2.6	0.87-1.13	/	/	/
P23	0.04-0.1	0.1-0.6	0.03	0.01	≤0.5	1.9-2.6	0.05-0.3	0.2-0.3	≤0.015	Cb(0.02-0.08) ,B(0.001-0.006)
										Al(≤0.03), W(1.45-1.75)
										Ni(≤0.4), Ti(0.005-0.060)
P24	0.05-0.1	0.3-0.7	0.02	0.01	0.15-0.45	2.2-2.6	0.9-1.1	0.2-0.3	≤0.012	Ti(0.06-0.1), Al(≤0.02)
										B(0.0015-0.007)
P36	0.1-0.17	0.8-1.2	0.03	0.025	0.25-0.50	≤0.30	0.25-0.50	≤0.02	≤0.02	Ni(1.0-1.3), Cu(0.5-0.8)
										Cb(0.015-0.045), Al(≤0.050)
P91	0.08-0.12	0.3-0.6	0.02	0.01	0.2-0.5	8.0-9.5	0.85-1.05	0.18-0.25	0.03-0.07	Ni(≤0.4), Al(≤0.02), Cb(0.06-0.1)
										Ti(≤0.01), Zr(≤0.01)
P92	0.07-0.13	0.3-0.6	0.02	0.01	≤0.50	8.5-9.5	0.3-0.6	0.15-0.25	0.03-0.07	Ni(≤0.4), AL(≤0.02), Cb(0.04-0.09)
										W(1.5-2.0), B(0.001-0.006)
										Ti(≤0.01), Zr(≤0.01)
P122	0.07-0.14	≤0.7	0.02	0.01	≤0.50	10.0-11.5	0.25-0.6	0.15-0.3	0.04-0.1	Ni(≤0.5), Al(≤0.02), Ti(≤0.01)
										W(1.5-2.5), Cu(0.3-1.7), Zr(≤0.01)
										Cb(0.04-0.1), B(0.0005-0.005)
P911	0.09-0.13	0.3-0.6	0.02	0.01	0.1-0.5	8.5-9.5	0.9-1.1	0.18-0.25	0.04-0.09	Ni(≤0.4), Cb(0.06-0.1)
										B(0.0003-0.006),Al(≤0.02)
										W(0.9-1.1),Ti(≤0.01),Zr(≤0.01)

Chrome Moly Pipes: Werkstoff vs EN vs ASTM

ASTM A335 pipe may be either hot finished or cold drawn with the finishing treatment as required in Grade P2 and P12 – The steel shall be made by coarse- grain melting practice. Specific limits, if any, on grain size or deoxidation practice shall be a matter of agreement between the manufacturer and purchaser.

Werkstoff /DIN	EN	ASTM
1.5415	16Mo3	A335 Grade P1
1.7335	13CrMo4-5	A335 Grade P11, P12
1.738	10CrMo9-10	A335 Grade P22
1.7362	X11CrMo5	A335 Grade P5
		A335 Grade P9
1.4903	X10CrMoVNb9-1	A335 Grade P91

Tensile Requirements

Tensile Strength, min., psi	P-5	P-9	P-11	P-22	P-91
ksi	60	60	60	60	85
MPa	415	415	415	415	585
Yield Strength, min., psi
ksi	30	30	30	30	60
MPa	205	205	205	205	415

Product Analysis At the request of the purchaser, an analysis of two pipe from each lot shall be made by the manufacturer. A lot of ASTM A335 pipe shall consist of the following: NPS Designator Under 2 400 or fraction thereof 2 to 5 200 or fraction thereof 6 and over 100 or fraction thereof. Note: ASTM A335 P91 shall not have a hardness not exceeding 250 HB/265 HV [25HRC].

Mechanical properties of ASTM A335

Grade	Tensile strength	Yield strength
P1,P2	380	205
P12	415	220
P23	510	400
P91	585	415
P92,P11	620	440
P122	620	400

It also enhances the corrosion resistance of steel, and inhibits pitting. Chromium (or chrome) is the essential constituent of stainless steel. Any steel with 12% or more Chrome is considered stainless. Chrome is virtually irreplaceable in resisting oxidation at elevated temperatures. Chrome raises the tensile, yield, and hardness at room temperatures. The composition chrome moly alloy steel pipe make it ideal for use in power plants, refineries, petro chemical plants, and oil field services where fluids and gases are transported at extremely high temperatures and pressures.

Alloy Steel Pipe

Material & Manufacture

Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below.

Heat Treatment

A / N+T

N+T / Q+T

N+T

Mechanical Tests Specified

Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test

For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.

For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.

Notes for Hardness Test

P11 shall not have a hardness not exceeding 250 HB/265 HV [25HRC].

Notes for Bend Test

For pipe whose diameter exceeds NPS 25 and whose diameter to wall thickness ratio is 7.0 or less shall be subjected to the bend test instead of the flattening test.

Other pipe whose diameter equals or exceeds NPS 10 may be given the bend test in place of the flattening test subject to the approval of the purchaser.

The bend test specimens shall be bent at room temperature through 180 without cracking on the outside of the bent portion.

FAQs About ASTM A335 Chrome Moly Pipe

Q1. What industries commonly use ASTM A335 Chrome Moly Pipe?

It is extensively used in power generation, petrochemicals, oil and gas, and aerospace industries.

Q2. Can ASTM A335 Chrome Moly Pipe withstand high pressures?

Yes, it is known for its ability to handle high-pressure environments effectively.

Q3. Is ASTM A335 Chrome Moly Pipe susceptible to corrosion?

While it can be prone to corrosion, proper coatings can make it highly resistant.

Q4. How is ASTM A335 Chrome Moly Pipe manufactured?

It is produced through a seamless manufacturing process, ensuring its robustness.

Q5. What sets ASTM A335 Chrome Moly Pipe apart from seamed pipes?

The seamless construction eliminates potential weak points, making it more reliable under pressure.